ICS21.140J22ZZB浙 江 制 造 团 体 标 准T/ZZB0686—2018高性能无压烧结碳化硅密封环High performance pressureless sintering silicon carbide seal rings2018-11-02发布2018-11-30实施浙江省品牌建设联合会发布 T/ZZB 0686—2018目次前言 ................................................................................ II123456789范围 .............................................................................. 1规范性引用文件 .................................................................... 1产品划分 .......................................................................... 1基本要求 .......................................................................... 1技术要求 .......................................................................... 2试验方法 .......................................................................... 3检验规则 .......................................................................... 4标志包装运输和贮存 ............................................................ 5质量承诺 .......................................................................... 5IT/ZZB 0686—2018前言本标准按照GB/T 1.1—2009给出的规则起草本标准由浙江省品牌建设联合会提出并归口本标准由宁波东联密封件有限公司牵头组织制定本标准主要起草单位：宁波东联密封件有限公司本标准参与起草单位：全国机械密封标准化技术委员会浙江工业大学合肥通用机械研究院中国兵器科学研究院宁波分院浙江省特种设备检验研究院宁波伏尔肯陶瓷科技有限公司宁波安睦密封科技有限公司台州东新密封有限公司奉化市飞固凯恒密封工程有限公司（排名不分先后）本标准主要起草人：叶传剑李平吴兆山彭旭东李香励永平陈刚徐梦戚明杰王树昕姜继新郑浦徐军本标准由宁波东联密封件有限公司负责解释IIT/ZZB 0686—2018高性能无压烧结碳化硅密封环1范围本标准规定了高性能无压烧结碳化硅密封环（以下简称密封环）的产品划分基本要求技术要求试验方法检验规则及标志包装运输贮存和质量承诺本标准适用于机械密封及特殊领域用无压烧结碳化硅密封环2规范性引用文件下列文件对于本文件的应用是必不可少凡是注日期的引用文件仅所注日期的版本适用于本文件凡是不注日期的引用文件其最新版本（包括所有的修改单）适用于本文件GB/T 191包装储运图示标志GB/T 1184—1996GB/T 1804—2000形状和位置公差未注公差值（eqv ISO 2768-2:1989）一般公差未注公差的线性和角度尺寸的公差（eqv ISO 2768-1:1989）GB/T 3045—2017普通磨料碳化硅化学分析方法（ISO 9286:1997MOD）GB/T 6569—2006精细陶瓷弯曲强度试验方法（ISO 14704:2000MOD）GB/T 8489GB/T 10700GB/T 16534GB/T 16535GB 25464精细陶瓷压缩强度试验方法精细陶瓷弹性模量试验方法工程陶瓷维氏硬度试验方法弯曲法工程陶瓷线热膨胀系数试验方法陶瓷工业污染物排